Brass Extruded Rods

Products Range

Brass Extruded Rods

Brass Square Extrusion Rods

Brass Flat Extrusion Rod

Hexagonal Extrusion Rods

Round Extrusion Rods

Brass Round Knurling Rods

Brass Hollow Rods

Round Hollow Rods

HEX Hollow Rods

FREE CUTTING BRASS RODS - Grade I

IS 319 / 89 NR. EQUIVALENT SPEC. BS 2874 / 86, CZ121PB3,JIS3250H C-3604, ASTMBC38500

Chemical Requirements (%)	Grade I
Copper	56.0 - 59.0 %
Lead	2.0 - 3.50 %
Iron	0.35% max.
Total Imp. Excl. Iron	0.70% max.
Zinc	Remainder

Physical Properties
Condition	Size	T. S. MPA	EL % Min
Annealed (O)	6-25	345	12
	25-50	315	17
	50 above	285	22
Half-Hard (HB)	6-12	405	4
	12-25	395	6
	25-50	355	12
Hard (HD)	50 above	325	17
	6-12	550	-
	12-25	490	4

Fabrication Properties
Capacity for being
Cold worked	Poor
Hot formed	Fair
Machinability Rating	100%
Suitability for Soldering	Excellent
Suitability for Brazing	Good

FREE CUTTING BRASS RODS - Grade II & III

IS 319 / 89 NR. EQUIVALENT SPEC. BS 2874 / 86 CZ124, JIS3250 H C-3602, ASTMBC36000

Chemical Requirements (%)	Grade II	Grade III
Copper	60.0 - 63.0 %	60.0 - 63.0 %
Lead	2.50 - 3.70 %	0.50 - 1.50 %
Iron	0.35 % max.	0.20 % max.
Total Imp. Excl. Iron	0.50 % max.	0.50 % max.
Zinc	Remainder	Remainder

Physical PropertiesGrade IIGrade III
Condition	Size	T. S. MPA	EL % Min	T. S. MPA	EL % Min
Annealed (O)	6-25	355	15	315	22
	25-50	305	20	285	27
	50 above	275	25	255	32
Half-Hard (HB)	6-12	395	7	355	8
	12-25	385	10	345	12
	25-50	345	15	305	22
Hard (HD)	50 above	315	20	285	27
	6-12	550	-	460	-
	12-25	485	4	400	4

Physical PropertiesGrade IIGrade III
Capacity for being
Cold worked	Poor	Fair
Hot formed	Fair	Excellent
Machinability Rating	90%	80%
Suitability for Soldering	Excellent	Excellent
Suitability for Brazing	Good	Excellent

FORGING BRASS RODS

EN 12164 : 1998

	A	B
Chemical Requirement(%)	CuZn39Pb3	CuZn40Pb2
Chemical Requirement(%)	CW614N	CW617N
Copper	57 - 59 %	57-59 %
Lead	2.5 - 3.5 %	1.6 - 2.5 %
Aluminum	0.05 % max	0.05 % max
Iron	0.30 % max	0.30 % max
Nickle	0.30 % max	0.30 % max
Tin	0.30 % max	0.30 % max
Total Imp.	0.20 % max	0.20 % max
Zinc	Remainder	Remainder

Physical Properties : (1/2 Hard)
Condition	Size	T. S. MPa	EL % Min.	Size	T. S. MPa	EL % Min.
Half-Hard (AB)	6 -14	400	15	6 -14	550
	14 - 40	380	18	14 - 40	500	8
	40 - 80	360	20	40 - 80	430	10

Fabrication Properties
Capacity for being
Cold Worked	Poor
Hot Formed	Excellent
Suitability for Soldering	Excellent
Suitability for Brazing	Good

FORGING BRASS RODS

BS 218

Chemical Requirement (%)
Copper	56.50 - 60.00 %
Lead	1.00 - 2.50 %
Iron	0.30 % max
Total Imp.	0.70 % max
Zinc	Remainder

Physical Properties
Rm - Tensile strength in Kg / mm2	32 min.
Elongation on 5.65 A%	25 min.

Fabrication Properties
Capacity for being
Cold Worked	Poor
Hot Formed	Excellent
Hot Forgebility Rating (Forging Brass - 100 )	100
Machinability Rating (IS 319-I 100)	80
Suitability for Soldering	Excellent
Suitability for Brazing	Good

FORGING BRASS RODS

IS – 6912 / 2005 FLB

Chemical Requirement (%)
Copper	56.50 - 60.00 %
Lead	0.60 - 2.00 %
Iron	0.30 % max.
Total Imp excl Fe	0.75 % max
Zinc	Remainder

Physical Properties
Rm - Tensile strength in Mpa	310 min.
Elongation on 5.65 A%	25 min.

Fabrication Properties
Capacity for being
Cold Worked	Poor
Hot Formed	Excellent
Hot Forgebility Rating (Forging Brass - 100 )	100
Machinability Rating (IS 319-I 100)	80
Suitability for Soldering	Excellent
Suitability for Brazing	Good

FORGING BRASS RODS

IS 3488 / 80 NR. EQUIVALENT SPEC. BS 2874 / 86 CZ122,ASTMBC37700

Chemical Requirements (%)	CuZn42Pb2	CuZn40Pb2
Copper	56.5 - 60.0 %	57.0 - 59.0 %
Lead	0.60 - 2.0 %	1.50 - 2.50 %
Iron	0.30 % max.	0.40 % max.
Total Imp. Excl. Iron	0.20% max	0.70 % max
Zinc	Remainder	Remainder

Physical Properties
Tensile Strength	380 Mpa Min	40 kg/mm2 min
Elongation %	25% Min	18% Min.
Izod Value	-	2.0 KJ Min.

Fabrication Properties
Capacity for being
Cold worked	Poor	Poor
Hot formed	Excellent	Excellent
Hot forgeability Rating	100%	100%
Machinability Rating	80%	80%
Suitability for Soldering	Excellent	Excellent
Suitability for Brazing	Good	Good

Anand Brass Components is a brass parts manufacturer and exporter based in Jamnagar, Gujarat, India. ISO 9001 certified. Manufacturing brass inserts, fittings, cable glands, CNC parts, fasteners, valves, and lead-free brass components for OEM buyers, importers, and distributors in the USA, UK, Europe, Middle East, and India since 1991.